Chemical Corrosion of S Y A L O N 101
SPECIES CONCENTRATION EXPOSURE TIME TEMPERATURE REACTION
  % in hours ° C NONE WEAK STRONG
Hydrochloric Acid 20 500 boiling X  
Nitric Acid 65 500 boiling X  
Sulphuric Acid 10 500 70 X  
Sulphuric Acid 85 500 20 X  
Orthophosphoric Acid 500 20 X  
Pyrophosphoric Acid 500 20 X  
Hydrofluoric Acid Concentrated 192 boiling   X
Sodium Hydroxide 20 500 20 X  
Sodium Hydroxide 50 115 boiling X  
Hydrofluoric & Nitric Acid Concentrated 68 boiling   X
GASES
Oxygene Air   500 X  
Oxygene Air   700   X  
Oxygene Air   1200     X
Chlorine Air 500 900 X    
MOLTEN SALTS + ALKALIES
Sodium Hydroxide   400   X  
Sodium Sulfate   1000   X
Sodium & Potassium Chloride   900   X
Chloride & Potassium Chloride   350   X  
Sodium & Zirconium Fluoride   650   X
MOLTEN METALS & ALLOYS
Copper 7 1150   X
Zinc 500 550 X  
Magnesium 500 750   X  
Aluminium 1000 950 X  
Tin 144 300 X  
Iron   2 1450     X
In case of combinations of above mentioned chemicals, the indicated temperatures and/or concentrations are NOT valid.